Phase transformation behavior of Cu-10Ni-3Al-0.8Si alloy

Shen, Leinuo, Li, Zhou, Zhao, Yuyuan ORCID: 0000-0003-2356-8435, Wang, Yang, Dong, Qiyi and Wang, Mengying (2016) Phase transformation behavior of Cu-10Ni-3Al-0.8Si alloy. MATERIALS CHEMISTRY AND PHYSICS, 173. pp. 421-428.

Text 2016_Matar_Chem_Phys_Cu_Alloy_final.pdf - Unspecified Download (1MB)

Abstract

Microstructure evolution of solution treated Cu-10Ni-3Al-0.8Si alloy aged at different temperatures was investigated and different transformation products were observed: modulated structure resulting from spinodal decomposition, L12 ordering of matrix, continuous Ni3Al precipitates, continuous δ-Ni2Si precipitates and discontinuous precipitates. Modulated structure, L12 ordering of matrix and micro-twins formed initially at 450 °C, while continuous Ni3Al and δ-Ni2Si particles precipitated soon. Increasing temperature led to the formation of discontinuous precipitates, dissolution of Ni3Al and cellular decomposition. The alloy showed excellent over-aging resistance at 450 °C because the Ni3Al and δ-Ni2Si precipitates grew very slowly and the addition of silicon hindered the precipitation of the coarsening NiAl phase.

Item Type:	Article
Uncontrolled Keywords:	Alloys, Precipitation, Electron microscopy, Microstructure
Depositing User:	Symplectic Admin
Date Deposited:	28 Apr 2016 10:24
Last Modified:	23 Feb 2023 05:18
DOI:	10.1016/j.matchemphys.2016.02.033
Related URLs:	Author Publisher
URI:	https://livrepository.liverpool.ac.uk/id/eprint/3000394