Micromechanical properties of canine femoral articular cartilage following multiple freeze-thaw cycles

Peters, Abby E, Comerford, Eithne J ORCID: 0000-0002-5244-6042, Macaulay, Sophie, Bates, Karl T ORCID: 0000-0002-0048-141X and Akhtar, Riaz ORCID: 0000-0002-7963-6874 (2017) Micromechanical properties of canine femoral articular cartilage following multiple freeze-thaw cycles JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 71. pp. 114-121. ISSN 1751-6161, 1878-0180

Text AbbyCaninePaper.pdf - Published version Download (420kB)

Abstract

Tissue material properties are crucial to understanding their mechanical function, both in healthy and diseased states. However, in certain circumstances logistical limitations can prevent testing on fresh samples necessitating one or more freeze-thaw cycles. To date, the nature and extent to which the material properties of articular cartilage are altered by repetitive freezing have not been explored. Therefore, the aim of this study is to quantify how articular cartilage mechanical properties, measured by nanoindentation, are affected by multiple freeze-thaw cycles. Canine cartilage plugs (n = 11) from medial and lateral femoral condyles were submerged in phosphate buffered saline, stored at 3–5 °C and tested using nanoindentation within 12 h. Samples were then frozen at −20 °C and later thawed at 3–5 °C for 3 h before material properties were re-tested and samples re-frozen under the same conditions. This process was repeated for all 11 samples over three freeze-thaw cycles. Overall mean and standard deviation of shear storage modulus decreased from 1.76 ± 0.78 to 1.21 ± 0.77 MPa (p = 0.91), shear loss modulus from 0.42 ± 0.19 to 0.39 ± 0.17 MPa (p=0.70) and elastic modulus from 5.13 ± 2.28 to 3.52 ± 2.24 MPa (p = 0.20) between fresh and three freeze-thaw cycles respectively. The loss factor increased from 0.31 ± 0.38 to 0.71 ± 1.40 (p = 0.18) between fresh and three freeze-thaw cycles. Inter-sample variability spanned as much as 10.47 MPa across freezing cycles and this high-level of biological variability across samples likely explains why overall mean “whole-joint” trends do not reach statistical significance across the storage conditions tested. As a result multiple freeze-thaw cycles cannot be explicitly or statistically linked to mechanical changes within the cartilage. However, the changes in material properties observed herein may be sufficient in magnitude to impact on a variety of clinical and scientific studies of cartilage, and should be considered when planning experimental protocols.

Item Type:	Article
Uncontrolled Keywords:	Canine, Femoral, Cartilage, Freezing, Nanoindentation
Depositing User:	Symplectic Admin
Date Deposited:	09 Mar 2017 11:37
Last Modified:	16 Jun 2026 04:02
DOI:	10.1016/j.jmbbm.2017.03.006
Related Websites:	Author Publisher
URI:	https://livrepository.liverpool.ac.uk/id/eprint/3006290
Disclaimer:	The University of Liverpool is not responsible for content contained on other websites from links within repository metadata. Please contact us if you notice anything that appears incorrect or inappropriate.