Inverse Vulcanized Polymers with Shape Memory, Enhanced Mechanical Properties, and Vitrimer Behavior

Yan, P ORCID: 0000-0001-7377-1808, Zhao, W ORCID: 0000-0003-0265-2590, Zhang, B ORCID: 0000-0002-9129-5793, Jiang, L, Petcher, S, Smith, JA, Parker, DJ, Cooper, AI ORCID: 0000-0003-0201-1021, Lei, J and Hasell, T ORCID: 0000-0003-4736-0604 (2020) Inverse Vulcanized Polymers with Shape Memory, Enhanced Mechanical Properties, and Vitrimer Behavior Angewandte Chemie, 132 (32). pp. 13473-13480. ISSN 0044-8249, 1521-3757

Text Yan_2020_ACIE.pdf - Published version Download (2MB) | Preview

Abstract

© 2020 The Authors. Published by Wiley-VCH Verlag GmbH & Co. KGaA. The invention of inverse vulcanization provides great opportunities for generating functional polymers directly from elemental sulfur, an industrial by-product. However, unsatisfactory mechanical properties have limited the scope for wider applications of these exciting materials. Here, we report an effective synthesis method that significantly improves mechanical properties of sulfur-polymers and allows control of performance. A linear pre-polymer containing hydroxyl functional group was produced, which could be stored at room temperature for long periods of time. This pre-polymer was then further crosslinked by difunctional isocyanate secondary crosslinker. By adjusting the molar ratio of crosslinking functional groups, the tensile strength was controlled, ranging from 0.14±0.01 MPa to 20.17±2.18 MPa, and strain was varied from 11.85±0.88 % to 51.20±5.75 %. Control of hardness, flexibility, solubility and function of the material were also demonstrated. We were able to produce materials with suitable combination of flexibility and strength, with excellent shape memory function. Combined with the unique dynamic property of S−S bonds, these polymer networks have an attractive, vitrimer-like ability for being reshaped and recycled, despite their crosslinked structures. This new synthesis method could open the door for wider applications of sustainable sulfur-polymers.

Item Type:	Article
Uncontrolled Keywords:	40 Engineering, 3403 Macromolecular and Materials Chemistry, 4016 Materials Engineering, 34 Chemical Sciences
Divisions:	Faculty of Science & Engineering > School of Physical Sciences
Depositing User:	Symplectic Admin
Date Deposited:	21 Apr 2021 09:05
Last Modified:	24 Jan 2026 02:38
DOI:	10.1002/ange.202004311
Related Websites:	Publisher
URI:	https://livrepository.liverpool.ac.uk/id/eprint/3119935
Disclaimer:	The University of Liverpool is not responsible for content contained on other websites from links within repository metadata. Please contact us if you notice anything that appears incorrect or inappropriate.