Doping of a high calcium oxide metaphosphate glass with titanium dioxide



Abou Neel, Ensanya A, Chrzanowski, Wojciech, Valappil, Sabeel P ORCID: 0000-0001-9646-8406, O'Dell, Luke A, Pickup, David M, Smith, Mark E, Newport, Robert J and Knowles, Jonathan C
(2009) Doping of a high calcium oxide metaphosphate glass with titanium dioxide. JOURNAL OF NON-CRYSTALLINE SOLIDS, 355 (16-17). pp. 991-1000.

[img] Text
Manuscript-Final_for_JNCS-edited_EAN.doc - Author Accepted Manuscript

Download (143kB)
[img] Text
Figures.doc - Unspecified

Download (4MB)
[img] Text
1165.pdf - Author Accepted Manuscript

Download (202kB)
[img] Text
1165_Figures.pdf - Unspecified

Download (228kB)

Abstract

This study investigates the effect of doping a high calcium oxide containing metaphosphate glass series (CaO)40(Na2O)10(P2O5)50 with TiO2 (1, 3, and 5 mol%). TiO2 incorporation increased the density and glass transition temperature while reduced the degradation rate (5 mol% in particular) by twofold compared with (CaO)30 system reported previously. This has been confirmed by ion release and the minimal pH changes. TiP2O7, NaCa(PO3)3 and CaP2O6 phases were detected for all TiO2-containing ceramics. XPS showed that the surface is composed of Ca, P, and Ti. Ti was recognized mainly as TiO2, but its total amount was lower than theoretical values. 31P magic angle spinning (MAS) NMR showed a downfield shift of the 31P lineshape with increasing TiO2, interpreted as an effect of the titanium cation rather than an increase in the phosphate network connectivity. FTIR showed that incorporation of TiO2 increased the strength of the phosphate chains, and the O/P ratio while introducing more Q1 units into the structure at the expense of the Q2 units. There were no differences, however, in surface topography roughness and free energies between these glasses. These results suggested that TiO2 and CaO were acting synergistically in producing glasses with controllable bulk and structural properties. © 2009 Elsevier B.V. All rights reserved.

Item Type: Article
Additional Information: Issue: 15 June 2009. Available online 4 May 2009.
Uncontrolled Keywords: Bioglass, Biomaterials, Chemical durability, Glass ceramics, X-ray diffraction, Glass transition, FTIR measurements, NMR, MAS-NMR and NQR
Subjects: ?? RK ??
Divisions: Faculty of Health and Life Sciences > Institute of Life Courses and Medical Sciences > School of Dentistry
Depositing User: Symplectic Admin
Date Deposited: 16 Oct 2009 08:42
Last Modified: 15 Dec 2022 07:29
DOI: 10.1016/j.jnoncrysol.2009.04.016
Related URLs:
URI: https://livrepository.liverpool.ac.uk/id/eprint/1165