Microstructure and mechanical properties of Cu-modified AlSi10Mg fabricated by Laser-Powder Bed Fusion



Garmendia, X, Chalker, S ORCID: 0000-0002-8855-2680, Bilton, M ORCID: 0000-0002-0475-2942, Sutcliffe, CJ and Chalker, PR ORCID: 0000-0002-2295-6332
(2020) Microstructure and mechanical properties of Cu-modified AlSi10Mg fabricated by Laser-Powder Bed Fusion. Materialia, 9. p. 100590.

Access the full-text of this item by clicking on the Open Access link.

Abstract

This influence of surface modification of powder feedstocks for additive manufacturing is assessed. Commercial AlSi10Mg powder was coated with 1 wt% copper using a copper formate precursor, which was reduced to metallic copper after vacuum heat treatment. Consolidated samples were produced using Laser-Powder Bed Fusion (L-PBF). Both the untreated and coated powders produced materials which exhibited high preferential crystal orientation, with grains aligned parallel to the build direction. The microstructure of the consolidated materials was characterized by SEM and TEM. The cells consisted of a α-Al matrix with copper particles decorating the intercellular region and eutectic silicon homogeneously dispersed in the cell boundary. The effect of the T6 heat treatment on the mechanical properties of the L-PBF-processed materials was a decrease in the strength. The specimens fabricated from coated powder exhibited an increased ultimate tensile strength (461 ± 0.2 MPa) and 12% elongation at break compared to the AlSi10Mg parts (346 ± 1.0 MPa) and 10% elongation. The study establishes the feasibility of modifying the composition of L-PBF-processed materials via the coating of powder feedstocks and that the coating additions can be exploited to enhance mechanical properties of parts after heat treatment.

Item Type: Article
Uncontrolled Keywords: Aluminium alloys, Laser-Powder Bed Fusion, Grain refinement, Metal matrix composites (MMCs), Strengthening mechanisms
Depositing User: Symplectic Admin
Date Deposited: 17 Jan 2020 11:52
Last Modified: 19 Jan 2023 00:09
DOI: 10.1016/j.mtla.2020.100590
Open Access URL: https://doi.org/10.1016/j.mtla.2020.100590
Related URLs:
URI: https://livrepository.liverpool.ac.uk/id/eprint/3070994